Semiconductor device including an ohmic layer

ABSTRACT

In an ohmic layer and methods of forming the ohmic layer, a gate structure including the ohmic layer and a metal wiring having the ohmic layer, the ohmic layer is formed using tungsten silicide that includes tungsten and silicon with an atomic ratio within a range of about 1:5 to about 1:15. The tungsten silicide may be obtained in a chamber using a reaction gas including a tungsten source gas and a silicon source gas by a partial pressure ratio within a range of about 1.0:25.0 to about 1.0:160.0. The reaction gas may have a partial pressure within a range of about 2.05 percent to about 30.0 percent of a total internal pressure of the chamber. When the ohmic layer is employed for a conductive structure, such as a gate structure or a metal wiring, the conductive structure may have a reduced resistance.

PRIORITY STATEMENT

This application is a divisional of U.S. application Ser. No. 11/332,476filed on Jan. 17, 2006, which claims priority under 35 USC § 119 toKorean Patent Application No. 2005-0004196 filed on Jan. 17, 2005, theentire contents of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Example embodiments of the present invention relate to an ohmic layer, amethod of forming an ohmic layer, a semiconductor device including anohmic layer and a method of forming a semiconductor device including anohmic layer. More particularly, example embodiments of the presentinvention relate to an ohmic layer reducing a resistance between siliconand metal, which may be used in a semiconductor device.

2. Description of the Related Art

As semiconductor devices have become highly integrated, sizes ofpatterns of semiconductor devices have been decreased and intervalsamong the patterns have been reduced. When conductive patterns, forexample, gate electrodes and/or bit lines have reduced sizes,resistances of the conductive patterns may increase.

Polysilicon doped with impurities may be used for a conventionalconductive pattern such as a gate electrode. However, a conductivepattern of doped polysilicon may not be employed in a highly integratedsemiconductor device having a high response speed because the reducedsize of the conductive pattern of doped polysilicon may cause theconductive pattern of doped polysilicon to have a relatively highresistance.

Therefore, a polycide structure was developed for forming a conductivepattern because the conductive pattern of a polycide structure may havea resistance lower than that of a conductive pattern of dopedpolysilicon. Conventionally, a polycide structure may include a dopedpolysilicon film and a refractory metal silicide film, for example, atungsten silicide film formed on a doped polysilicon film. However, aconductive pattern of a polycide structure may not be employed in aconventional semiconductor device requiring an exceedingly lowresistance, although the conductive pattern of the polycide structurehas the low resistance.

Considering the above-mentioned problem, a conductive pattern includinga polysilicon film and a metal film has been developed for aconventional semiconductor device. However, a metal film of a conductivepattern may be easily silicided in a formation of the metal film on apolysilicon film, so a barrier layer may be formed between thepolysilicon film and the metal film in order to reduce a silicidationreaction between the polysilicon film and the metal film. Further, anohmic layer may be formed between a polysilicon film and a metal film toreduce a total resistance of a conductive pattern.

An ohmic layer is generally formed between a metal wiring and a siliconlayer or a silicon substrate when a metal wiring is formed on asubstrate. For example, a prior art method of forming a gate electrodemay include a polysilicon layer pattern and a tungsten layer pattern. Inparticular, a prior art gate electrode may include a polysilicon layerpattern, a tungsten silicide layer pattern, a diffusion barrier layerpattern and the tungsten layer pattern. A tungsten silicide layerpattern of the prior art gate electrode may include tungsten and siliconwith an atomic ratio in a range of about 1:2 to about 1:3.

When a tungsten silicide layer pattern having tungsten and silicon bythe atomic ratio in the range of about 1:2 to about 1:3 is formedbetween a polysilicon layer pattern and a tungsten layer pattern,however, ingredients in a diffusion barrier layer pattern may be easilydecomposed in a succeeding thermal process so that the tungsten layerpattern may be easily silicided, and then the tungsten layer pattern maybe converted into a silicide layer pattern. When a tungsten layerpattern is converted into a silicide layer pattern, a gate electrode maynot have a desired low resistance. Additionally, a volume of a tungstenlayer pattern is reduced when the tungsten silicide layer pattern issilicided so that a void may be generated at an interface between apolysilicon layer pattern and a tungsten silicide layer pattern.

SUMMARY OF THE INVENTION

Example embodiments of the present invention provide an ohmic layer. Theohmic layer may reduce an interface resistance between two layersincluding materials different from each other.

Example embodiments of the present invention provide a method of formingan ohmic layer. The ohmic layer may reduce an interface resistancebetween two layers including materials different from each other.

Example embodiments of the present invention provide a gate structurehaving an ohmic layer. The ohmic layer of the gate structure may reducean interface resistance between two layers including materials differentfrom each other.

Example embodiments of the present invention provide a method of forminga gate structure having an ohmic layer. The ohmic layer of the gatestructure may reduce an interface resistance between two layersincluding materials different from each other.

Example embodiments of the present invention provide a metal wiringhaving an ohmic layer. The ohmic layer of the metal wiring may reduce aninterface resistance between two layers including materials differentfrom each other.

Example embodiments of the present invention provide a method of forminga metal wiring having an ohmic layer. The ohmic layer of the metalwiring may reduce an interface resistance between two layers includingmaterials different from each other.

An example embodiment of the present invention provides an ohmic layerin a semiconductor device. The ohmic layer may include a tungstensilicide layer that includes tungsten and silicon with an atomic ratiowithin a range of about 1:5 to about 1:15.

An example embodiment of the present invention provides a method offorming an ohmic layer in a semiconductor device. The method may includeforming a tungsten silicide layer on a substrate. The tungsten silicidelayer may include tungsten and silicon with an atomic ratio within arange of about 1:5 to about 1:15.

BRIEF DESCRIPTION OF THE DRAWINGS

Example embodiments of the present invention will be more clearlyunderstood from the description of example embodiments of the presentinvention, taken in conjunction with the accompanying drawings. Thedrawings are not necessarily to scale, emphasis instead being placedupon illustrating the principles of the invention.

FIG. 1 is a cross-sectional view illustrating a transistor including anohmic layer pattern in accordance with an example embodiment of thepresent invention;

FIGS. 2 to 5 are cross-sectional views illustrating a method ofmanufacturing a transistor in accordance with an example embodiment ofthe present invention;

FIG. 6 is a cross-sectional view illustrating a metal wiring includingan ohmic layer in accordance with an example embodiment of the presentinvention;

FIGS. 7 and 8 are cross-sectional views illustrating a method of forminga metal wiring in accordance with an example embodiment of the presentinvention;

FIGS. 9 and 10 are electron microscopic photographs showing gatestructures according to Examples 1 and 2; and

FIG. 11 is an electron microscopic photograph showing a gate structureaccording to Comparative Example 1.

DESCRIPTION OF EXAMPLE EMBODIMENTS

Example embodiments are described more fully hereinafter with referenceto the accompanying drawings, in which the example embodiments areshown. Example embodiments may, however, be embodied in many differentforms and should not be construed as limited to the example embodimentsset forth herein. Rather, these example embodiments are provided so thatthis disclosure will be thorough and complete, and will fully convey thescope of the present invention to those skilled in the art. In thedrawings, the sizes and relative sizes of layers and regions may beexaggerated for clarity.

It will be understood that when an element or layer is referred to asbeing “on”, “connected to” or “coupled to” another element or layer, itcan be directly on, connected or coupled to the other element or layeror intervening elements or layers may be present. In contrast, when anelement is referred to as being “directly on,” “directly connected to”or “directly coupled to” another element or layer, there are nointervening elements or layers present. Like numbers refer to likeelements throughout the figures. As used herein, the term “and/or”includes any and all combinations of one or more of the associatedlisted items.

It will be understood that, although the terms first, second, third,etc. may be used herein to describe various elements, components,regions, layers and/or sections, these elements, components, regions,layers and/or sections should not be limited by these terms. These termsare only used to distinguish one element, component, region, layer orsection from another region, layer or section. Thus, a first element,component, region, layer or section discussed below could be termed asecond element, component, region, layer or section without departingfrom the teachings of the present invention.

Spatially relative terms, such as “beneath”, “below”, “lower”, “above”,“upper” and the like, may be used herein for ease of description todescribe one element or feature's relationship to another element(s) orfeature(s) as illustrated in the figures. It will be understood that thespatially relative terms are intended to encompass differentorientations of the device in use or operation in addition to theorientation depicted in the figures. For example, if the device in thefigures is turned over, elements described as “below” or “beneath” otherelements or features would then be oriented “above” the other elementsor features. Thus, the example term “below” can encompass both anorientation of above and below. The device may be otherwise oriented(rotated 90 degrees or at other orientations) and the spatially relativedescriptors used herein interpreted accordingly.

The terminology used herein is for the purpose of describing particularembodiments only and is not intended to be limiting of the presentinvention. As used herein, the singular forms “a”, “an” and “the” areintended to include the plural forms as well, unless the context clearlyindicates otherwise. It will be further understood that the terms“includes”, “comprises”, “including” and/or “comprising,” when used inthis specification, specify the presence of stated features, integers,steps, operations, elements, and/or components, but do not preclude thepresence or addition of one or more other features, integers, steps,operations, elements, components, and/or groups thereof.

Example embodiments of the present invention are described herein withreference to cross-section illustrations that are schematicillustrations of example embodiments (and intermediate structures) ofthe present invention. As such, variations from the shapes of theillustrations as a result, of manufacturing techniques and/ortolerances, for example, are to be expected. Thus, example embodimentsof the present invention should not be construed as limited to theparticular shapes of regions illustrated herein and are to includedeviations in shapes that result, for example, from manufacturing. Forexample, an implanted region illustrated as a rectangle will, typically,have rounded or curved features and/or a gradient of implantconcentration at its edges rather than a binary change from implanted tonon-implanted region. Likewise, a buried region formed by implantation,for example, may result in some implantation in the region between theburied region and the surface through which the implantation takesplace. Thus, the regions illustrated in the figures are schematic innature and their shapes are not intended to illustrate the actual shapeof a region of a device and are not intended to limit the scope of thepresent invention.

Unless otherwise defined, all terms (including technical and scientificterms) used herein have the same meaning as commonly understood by oneof ordinary skill in the art to which this invention belongs. It will befurther understood that terms, such as those defined in commonly useddictionaries, should be interpreted as having a meaning that isconsistent with their meaning in the context of the relevant art andwill not be interpreted in an idealized or overly formal sense unlessexpressly so defined herein.

A resistance reduction layer (hereinafter, referred to as “an ohmiclayer”) according to an example embodiment of the present invention mayhave a tungsten silicide layer that includes tungsten and silicon withan atomic ratio in a range of about 1:5 to about 1:15. Further, theatomic ratio of tungsten and silicon in the ohmic layer of tungstensilicide according to an example embodiment of the present invention maybe within a range of about 1:7 to about 1:10.

In some example embodiments of the present invention, a tungstensilicide layer serving as the ohmic layer may be obtained in a chamberusing a reaction gas that includes a tungsten source gas and a siliconsource gas by a partial pressure ratio within a range of about 1.0:25.0to about 1.0:160.0. Further, the reaction gas may have a partialpressure within a range of about 2.05 percent to about 30.0 percent of atotal internal pressure of the chamber.

In some example embodiments of the present invention, the tungstensilicide layer may be obtained by a sputtering process using a tungstensilicide target that includes tungsten and silicon with an atomic ratiowithin a range of about 1:5 to about 1:15.

In a method of forming an ohmic layer including tungsten silicideaccording to an example embodiment of the present invention, after asubstrate is loaded into a chamber, a tungsten silicide layer is formedon the substrate as the ohmic layer. The tungsten silicide layer mayinclude tungsten and silicon with an atomic ratio within a range ofabout 1:5 to about 1:15

In a process for forming a tungsten silicide layer according to anexample embodiment of the present invention, a reaction gas includingtungsten and silicon source gases may be introduced into a chamber. Thereaction gas may have a partial pressure within a range of about 2.05percent to about 30.0 percent of the total internal pressure of thechamber. A partial pressure ratio between the tungsten source gas andthe silicon source gas in the reaction gas may be within a range ofabout 1.0:25.0 to about 1.0:160.0.

In example embodiments of the present invention, a tungsten source gasmay include tungsten fluoride (WF₆), for example. A silicon source gasmay include dichlorosilane (SiH₂Cl₂; DCS) or silane (SiH₄), for example.

In example embodiments of the present invention, an inert gas may beintroduced into a chamber to carry a reaction gas and/or to adjustprocess conditions for forming a tungsten silicide layer in the chamber.The inert gas may have a partial pressure within a range of about 70percent to about 97.95 percent of a total internal pressure of thechamber.

According to an example embodiment of the present invention, a chambermay have a total internal pressure within a range of about 0.5 Torr toabout 5.0 Torr. According to another example embodiment of the presentinvention, a total internal pressure of the chamber is within a range ofabout 0.5 Torr to about 1.5 Torr.

In example embodiments of the present invention, a tungsten silicidelayer serving as an ohmic layer may be obtained by a physical vapordeposition (PVD) process, for example, a sputtering process using atarget that includes tungsten and silicon with an atomic ratio within arange of about 1:5 to about 1:15.

FIG. 1 is a cross-sectional view illustrating a transistor including anohmic layer pattern in accordance with an example embodiment of thepresent invention.

Referring to FIG. 1, a transistor may include a gate insulation layer102 formed on a substrate 100. An active region and a field region maybe defined on a substrate 100 by an isolation process, for example, ashallow trench isolation (STI) process.

The gate insulation layer 102 may include an oxide, for example, siliconoxide. Alternatively, the gate insulation layer 102 may include amaterial having a dielectric constant substantially higher than that ofsilicon oxide. For example, the gate insulation layer 102 may include,but is not limited to, HfO₂, ZrO₂, Ta₂O₅, Y₂O₃, Nb₂O₅, Al₂O₃, TiO₂,CeO₂, In₂O₃, RuO₂, MgO, SrO, B₂O₃, SnO₂, PbO, PbO₂, Pb₃O₄, V₂O₃, La₂O₃,Pr₂O₃, Sb₂O₃, Sb₂O₅, CaO, etc., or mixtures thereof.

A transistor according to an example embodiment of the present inventionmay include a conductive structure, for example, a gate structure thathas a polysilicon layer pattern 104 a, a tungsten silicide layer pattern106 a, a barrier layer pattern 108 a and a tungsten layer pattern 110 asequentially formed on the gate insulation layer 102. The polysiliconlayer pattern 104 a may correspond to a first conductive layer patternand a tungsten layer pattern 110 a may correspond to a second conductivelayer pattern. A transistor may also include a hard mask pattern 112formed on the tungsten layer pattern 110 a. Further, a transistor mayinclude a spacer 114 formed on a sidewall of the gate structure and asidewall of the hard mask pattern 112.

P type impurities or N type impurities may be doped in the polysiliconlayer pattern 104 a. When the transistor is a P type transistor, the Ptype impurities are doped in the polysilicon layer pattern 104 a. The Ntype impurities are doped in the polysilicon layer pattern 104 a whenthe transistor is an N type transistor.

According to an example embodiment of the present invention, thetungsten silicide layer pattern 106 a may enhance adhesion strengthbetween the polysilicon layer pattern 104 a and the tungsten layerpattern 110 a. The tungsten silicide layer pattern 106 a serves as anohmic layer pattern (that is, a resistance reduction layer pattern) thatmay reduce a contact resistance between the polysilicon layer pattern104 a and the tungsten layer pattern 110 a. The tungsten silicide layerpattern 106 a may include tungsten and silicon with an atomic ratiowithin a range of about 1:5 to about 1:15. The tungsten silicide layerpattern 106 a may have a thickness of about 30 Å to about 200 Å.

The tungsten silicide layer pattern 106 a may be formed under processconditions so that a silicidation reaction between the tungsten layerpattern 110 a and the polysilicon layer pattern 104 a may be reducedand/or prevented in succeeding processes, for example, a process offorming the barrier layer 108 a, a process of forming the tungsten layerpattern 110 a and a thermal process for forming the transistor.According to an example embodiment of the present invention, an atomicratio of tungsten and silicon included in the tungsten silicide layerpattern 106 a may be adjusted and a thickness of the tungsten silicidelayer pattern 106 a may be controlled to reduce and/or prevent theabove-mentioned silicidation reaction.

In an example embodiment of the present invention, because asilicidation process may be caused by a partial thermal decomposition ofingredients in the barrier layer pattern 108 a in a succeeding thermalprocess, a content of silicon included in the tungsten silicide layerpattern 106 a may be increased to reduce and/or minimize the thermaldecomposition of ingredients in the barrier layer pattern 108 a.However, a gate electrode including a tungsten silicide layer pattern106 a may have an undesirably large resistance when the content ofsilicon in the tungsten silicide layer pattern 106 a is excessivelyincreased. The content of silicon in the tungsten silicide layer pattern106 a may be adjusted so the atomic ratio of tungsten and silicon in thetungsten silicide layer pattern 106 a may be in a range of about 1:5 toabout 1:15 to reduce and/or prevent a silicidation reaction and anincrease of the resistance of the gate electrode. For example, thetungsten silicide layer pattern 106 a may be adjusted to includetungsten and silicon with an atomic ratio within a range of about 1:7 toabout 1:10.

Further, the barrier layer pattern 108 a may be damaged in a succeedingthermal process. The damage is at least partly related to a thickness ofthe tungsten silicide layer pattern 106 a. For example, a thinnertungsten silicide layer pattern 106 a may reduce and/or minimize asilicidation reaction between the polysilicon layer pattern 104 a andthe tungsten layer pattern 110 a. When the tungsten silicide layerpattern 106 a has a thickness of above about 200 Å, most of the tungstenin the tungsten layer pattern 110 a may be silicided in the succeedingthermal process because the barrier layer pattern 108 a is damaged.Thus, according to an example embodiment of the present invention, thetungsten silicide layer pattern 106 a may have a thickness less thanabout 200 Å. Conversely, a resistance of the gate electrode mayincreased because the tungsten silicide layer pattern 106 a may notproperly serve as the ohmic layer pattern if the tungsten silicide layerpattern 106 a has a thickness less than about 30 Å. Therefore, accordingto an example embodiment of the present invention, the tungsten silicidelayer pattern 106 a may have a thickness in a range of about 30 Å toabout 200 Å.

In an example embodiment of the present invention, the tungsten silicidelayer pattern 106 a may be formed on the polysilicon layer pattern 104 ain a chamber using a reaction gas including a tungsten source gas and asilicon source gas. The tungsten source gas and the silicon source gasmay be provided onto the polysilicon layer pattern 104 a by a partialpressure ratio within a range of about 1.0:25.0 to about 1.0:160.0.Further, the reaction gas may be introduced into the chamber to adjustan internal pressure of the chamber. For example, the reaction gas mayhave a partial pressure within a range of about 2.05 percent to about30.0 percent of the internal pressure in the chamber.

In an example embodiment of the present invention, the tungsten silicidelayer pattern 106 a may be formed by a sputtering process using atungsten silicide target that includes tungsten and silicon with anatomic ratio within a range of about 1:5 to about 1:15.

Referring now to FIG. 1, the barrier layer pattern 108 a may include ametal nitride. The barrier layer pattern 108 a may reduce and/or preventdiffusion of tungsten included in the tungsten layer pattern 110 a. Forexample, the barrier layer pattern 108 a may include tungsten nitride,titanium nitride, tantalum nitride, boron nitride, etc.

The hard mask pattern 112 may include a nitride, for example, siliconnitride. As shown in FIG. 1, the spacer 114 may extend from the gateinsulation layer 102 to a sidewall of the hard mask pattern 112.

The transistor may also include source/drain regions 116 formed atportions of the substrate 100 adjacent to the gate electrode.

As described above, a gate electrode according to an example embodimentof the present invention may have a reduced resistance because the gateelectrode includes an ohmic layer pattern, for example, the tungstensilicide layer pattern 106 a and a conductive layer pattern, forexample, the tungsten layer pattern 110 a. Further, the tungsten layerpattern 110 a of the gate electrode may not be silicided due to thetungsten silicide layer pattern 106 a interposed between the tungstenlayer pattern 110 a and the polysilicon layer pattern 104 a because thetungsten silicide layer pattern 106 a has a properly adjusted thicknessand includes tungsten and silicon by the atomic ratio within a range ofabout 1:5 to about 1:15.

FIGS. 2 to 5 are cross-sectional views illustrating a method ofmanufacturing a transistor in accordance with an example embodiment ofthe present invention.

Referring to FIG. 2, an active region and a field region may be definedon a semiconductor substrate 100 through an isolation process.

A gate insulation layer 102 may be formed on a substrate 100. The gateinsulation layer 102 including silicon oxide may be formed on thesubstrate 100 by a thermal oxidation process. Alternatively, the gateinsulation layer 102 may be formed on the substrate 100 including amaterial having a high dielectric constant by a chemical-vapordeposition (CVD) process, an atomic layer deposition (ALD) process, asputtering process, a high-density plasma chemical-vapor deposition(HDP-CVD) process, etc.

A polysilicon layer 104 may be formed on the gate insulation layer 102positioned on the substrate 100 as a first conductive layer. Thepolysilicon layer 104 may be doped with P type impurities and/or N typeimpurities using a diffusion process, an ion implantation process, anin-situ doping process, etc.

In an example embodiment of the present invention, the polysilicon layer104 may be doped with the P type impurities, for example, boron (B),boron fluoride (BF₂) and/or indium (In) when a transistor is a P typetransistor.

In another example embodiment of the present invention, the polysiliconlayer 104 may be doped with the N type impurities, for example,phosphorus (P) and/or arsenic (As) when the transistor is an N typetransistor.

Referring to FIG. 3, a tungsten silicide layer 106 may be formed on thepolysilicon layer 104. The tungsten silicide layer 106 serves as anohmic layer that reduces a resistance of a gate electrode of thetransistor. According to an example embodiment of the present invention,the tungsten silicide layer 106 may include tungsten and silicon with anatomic ratio within a range of about 1:5 to about 1:15. According toanother example embodiment of the present invention, an atomic ratiobetween tungsten and silicon in the tungsten silicide layer 106 may bewithin a range of about 1:7 to about 1:10.

The tungsten silicide layer 106 according to an example embodiment ofthe present invention may have a thickness within a range of about 30 Åto about 200 Å. According to another example embodiment of the presentinvention, a thickness of the tungsten silicide layer 106 may be withina range of about 50 Å to about 100 Å. The tungsten silicide layer 106may be formed by a CVD process, an ALD process, an HDP-CVD process, asputtering process, an evaporation process, a PLD process, etc.

In an example embodiment of the present invention, the tungsten silicidelayer 106 may be formed by a CVD process. In a CVD process forming thetungsten silicide layer 106, the substrate 100 having the polysiliconlayer 104 thereon is loaded into a chamber of a chemical-vapordeposition apparatus. A reaction gas including a tungsten source gas anda silicon source is introduced into the chamber. The reaction gas mayhave a partial pressure within a range of about 2.05 percent to about30.0 percent of a total internal pressure of the chamber. Additionally,the tungsten source gas may have a partial pressure sufficiently lowerthan that of the silicon source gas to form the tungsten silicide layer106 that includes tungsten and silicon with an atomic ratio within arange of about 1:5 to about 1:15.

If a partial pressure ratio between the tungsten source gas and thesilicon source gas is too low, a content of tungsten in the tungstensilicide layer 106 may exceed a previously set content of tungsten inthe tungsten silicide layer 106 and as a result, the tungsten silicidelayer 106 may not effectively serve as an ohmic layer. Further, if apartial pressure ratio between the tungsten source gas and the siliconsource gas is too large, a content of silicon in the tungsten silicidelayer 106 may exceed a previously set content of silicon in the tungstensilicide layer 106 and as a result, the tungsten silicide layer 106 maynot have a composition suitable for acting as the ohmic layer. Accordingto an example embodiment of the present invention, a partial pressureratio between the tungsten source gas and the silicon source gas is in arange of about 1.0:25.0 to about 1.0:160.0. According to another exampleembodiment of the present invention, a partial pressure ratio betweenthe tungsten source gas and the silicon source gas may be in a range ofabout 1.0:25.0 to about 1.0:30.0.

In an example embodiment of the present, the tungsten source gas mayinclude tungsten fluoride (WF₆) and the silicon source gas may includedichlorosilane (SiH₂Cl₂; DCS) or silane (SiH₄), for example.

In an example embodiment of the present invention, an inert gas may beintroduced into the chamber as a carrier gas to transport a reaction gasinto the chamber and to control the total internal pressure of thechamber. For example, the inert gas may have a partial pressure in arange of about 70 percent to about 97.95 percent of the total internalpressure in the chamber. The inert gas may include an argon (Ar) gas, ahelium (He) gas, a nitrogen (N₂) gas, etc.

In an example embodiment of the present invention, a chamber may have atotal internal pressure in a range of about 0.5 Torr to about 5.0 Torr,while a CVD process for forming the tungsten silicide layer 106 isperformed. According to an example embodiment of the present invention,a total internal pressure of the chamber may be in a range of about 0.5Torr to about 1.5 Torr.

In an example embodiment of the present invention, the tungsten silicidelayer 106 may be formed by a physical vapor deposition (PVD) process,for example, a sputtering process using a target that includes tungstenand silicon with an atomic ratio in a range of about 1:5 to about 1:15.

Referring to FIG. 4, a barrier layer 108 may be formed on the tungstensilicide layer 106. The barrier layer 108 may reduce and/or preventdiffusion of metal atoms in succeeding processes. The barrier layer 108may be formed using a nitride, for example, tungsten nitride, titaniumnitride, tantalum nitride, boron nitride, etc. Further, the barrierlayer 108 may be formed by a CVD process, an ALD process, a sputteringprocess, an evaporation process, a PLD process, etc. The barrier layer108 may have a resistance substantially higher than that of a tungstenlayer 110 succeedingly formed on the barrier layer 108. A thickness ofthe barrier layer 108 may be reduced and/or minimized to a thicknessthat sufficiently reduces and/or prevents the diffusion of the metalatoms. According to an example embodiment of the present invention, thebarrier layer 108 has a thickness in a range of about 30 Å to about 100Å.

The tungsten layer 110 may be formed on the barrier layer 108 as asecond conductive layer. According to an example embodiment of thepresent invention, the tungsten layer 110 may have a thickness in arange of about 200 Å to about 800 Å measured from an upper face of thebarrier layer 108. The tungsten layer 110 may be formed by a CVD processor a PVD process.

A hard mask layer (not shown) may be formed on the tungsten layer 110.The hard mask layer may be formed using a nitride, for example, siliconnitride. The hard mask layer may be patterned by a photolithographyprocess to form a hard mask pattern 112 on the tungsten layer 110.

Referring to FIG. 5, the tungsten layer 110, the barrier layer 108, thetungsten silicide layer 106 and the polysilicon layer 104 may besequentially etched using the hard mask pattern 112 as an etching maskto form a polysilicon layer pattern 104 a, a tungsten silicide layerpattern 106 a, a barrier layer pattern 108 a and a tungsten layerpattern 110 a on the gate insulation layer 102. The gate insulationlayer 102, the polysilicon layer pattern 104 a, the tungsten silicidelayer pattern 106 a, the barrier layer pattern 108 a, the tungsten layerpattern 110 a and the hard mask pattern 112 may be collectivelyreferenced to as a gate structure.

In an example embodiment of the present invention, a sidewall of thegate structure may be selectively oxidized at a temperature in a rangeof about 800° C. to about 1,000°. This thermal oxidation process isoften referred to as a re-oxidation process. In a re-oxidation processfor the gate structure according to an example embodiment of the presentinvention, the tungsten layer pattern 110 a and the tungsten silicidelayer pattern 106 a are not oxidized.

As described above, the tungsten layer pattern 110 a may not react withthe polysilicon layer pattern 104 a when a temperature greater thanabout 800° C. is used in a thermal process for example, the re-oxidationprocess because the tungsten silicide layer pattern 106 a includingtungsten and silicon by the atomic ratio in a range of about 1:5 toabout 1:15 may effectively reduce and/or prevent a silicidation reactionbetween the tungsten layer pattern 110 a and the polysilicon layerpattern 104 a. Accordingly, an electrical defect in a gate structure,for example, an excessive increase of resistance due to an undesiredsilicide layer pattern may be avoided because the tungsten layer pattern110 a may not be converted to an undesired silicide layer pattern.Therefore, the gate structure according to an example embodiment of thepresent invention may have improved electrical characteristics.

According to an example embodiment of the present invention, after aspacer 114 (see FIG. 1) is formed on the sidewall of the gate structure,source/drain regions 116 (see FIG. 1) may be formed at portions of thesubstrate 100 adjacent to the gate structure, thereby forming atransistor on the substrate 100.

FIG. 6 is a cross-sectional view illustrating a metal wiring includingan ohmic layer in accordance with an example embodiment of the presentinvention.

Referring to FIG. 6, an insulation layer 204 or an insulating interlayermay be formed on a substrate 200. A contact hole (not shown) may beformed through the insulation layer 204 to expose a portion of thesubstrate 200. The contact hole may expose a contact region formed at anupper portion of the substrate 200. The contact region of the substrate200 may be formed by doping P type impurities or N type impurities.

A metal wiring may include a tungsten silicide layer pattern 206 aformed on a sidewall and on a bottom face of the contact hole. Thetungsten silicide layer pattern 206 a serves as an ohmic layer patternthat reduces a contact resistance between the contact region and aconductive layer pattern formed on the tungsten silicide layer pattern206 a. The tungsten silicide layer pattern 206 a may include tungstenand silicon with an atomic ratio in a range of about 1:5 to about 1:15.For example, the tungsten silicide layer pattern 206 a may includetungsten and silicon with an atomic ratio of about 1:7 to about 1:10.The tungsten silicide layer pattern 206 a may have a thickness in arange of about 30 Å to about 200 Å.

In an example embodiment of the present invention, the tungsten silicidelayer pattern 206 a may be formed in a chamber using a reaction gas thatincludes a tungsten source gas and a silicon source gas by a partialpressure ratio in a range of about 1.0:25.0 to about 1.0:160.0. Thereaction gas may have a partial pressure in a range of about 2.05percent to about 30.0 percent of a total internal pressure in thechamber.

In another example embodiment of the present invention, the tungstensilicide layer pattern 206 a may be formed by a sputtering process usinga tungsten silicide target that includes tungsten and silicon with anatomic ratio in a range of about 1:5 to about 1:15.

The metal wiring according to an example embodiment of the presentinvention may include a barrier layer pattern 208 a formed on thetungsten silicide layer pattern 206 a. The barrier layer pattern 208 amay include a nitride, for example, tungsten nitride, titanium nitride,tantalum nitride, boron nitride, etc. The metal wiring may include ametal layer pattern 210 a formed on the barrier layer pattern 208 a toat least partially fill the contact hole. The metal layer pattern 210 amay correspond to the conductive layer pattern and may include tungsten.

FIGS. 7 and 8 are cross-sectional views illustrating a method of forminga metal wiring in accordance with an example embodiment of the presentinvention.

Referring to FIG. 7, an insulation layer 204 and/or an insulatinginterlayer may be formed on a substrate 200. A lower structure may beformed between the substrate 200 and the insulation layer 204. The lowerstructure may include a contact region, a pad, a plug, a conductivepattern and/or a transistor.

The insulation layer 204 may be partially etched to form a contact hole203 that exposes a portion of the substrate 200 and/or the lowerstructure.

A tungsten silicide layer 206 may be formed on a sidewall, a bottom faceof the contact hole 203, and/or on the insulation layer 204. Thetungsten silicide layer 206 may include tungsten and silicon with anatomic ratio of about 1:5 to about 1:15. The tungsten silicide layer 206may have a thickness of about 30 Å to about 200 Å measured from an upperface of the insulation layer 204. The tungsten silicide layer 206 may beformed by a process substantially the same as the process described withreference to FIG. 3.

Referring to FIG. 8, a barrier layer 208 may be formed on the tungstensilicide layer 206. The barrier layer 208 may be formed using a nitride,for example, tungsten nitride, titanium nitride, tantalum nitride, boronnitride, etc.

As shown in FIG. 8, a metal layer 210 may be formed on the barrier layer208 to at least partially fill the contact hole 203. The metal layer 210may be formed using tungsten.

The metal layer 210, the barrier layer 208 and the tungsten silicidelayer 206 may be partially removed until the insulation layer 204 isexposed to subsequently form a tungsten silicide layer pattern, abarrier layer pattern and a metal layer pattern. The metal layer 210,the barrier layer 208 and the tungsten silicide layer 206 may bepartially removed by a chemical mechanical polishing (CMP) process, anetch-back process or a combination process of CMP and etch-back.

Hereinafter, various Examples and Comparative Examples of transistorsillustrating the teachings of the present invention will be described.

Example 1

A transistor of Example 1 included a gate insulation layer formed on asubstrate. The transistor further included a gate structure that had apolysilicon layer pattern doped with P type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:5. The transistor includedsource/drain regions formed at portions of the substrate adjacent to thegate structure. The source/drain regions were doped with P typeimpurities.

Example 2

A transistor of Example 2 had a gate insulation layer formed on asubstrate. The transistor included a gate structure that had apolysilicon layer pattern doped with P type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:7. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withP type impurities.

Example 3

A transistor of Example 3 had a gate insulation layer formed on asubstrate. The transistor included a gate structure that had apolysilicon layer pattern doped with P type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:8. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withP type impurities.

Example 4

A transistor of Example 4 had a gate insulation layer formed on asubstrate. The transistor included a gate structure that had apolysilicon layer pattern doped with N type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:5. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withN type impurities.

Example 5

A transistor of Example 5 had a gate insulation layer formed on asubstrate. The transistor included a gate structure that had apolysilicon layer pattern doped with N type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:7. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withN type impurities.

Example 6

A transistor of Example 6 included a gate insulation layer formed on asubstrate. The transistor had a gate structure that had a polysiliconlayer pattern doped with N type impurities, a tungsten silicide layerpattern, a barrier layer pattern, a metal layer pattern and a hard maskpattern sequentially formed on the gate insulation layer. Here, thetungsten silicide layer pattern included tungsten and silicon with anatomic ratio of about 1:8. The transistor further included source/drainregions formed at portions of the substrate adjacent to the gatestructure. The source/drain regions were doped with N type impurities.

Comparative Example 1

A transistor of Comparative Example 1 included a gate insulation layerformed on a substrate. The transistor had a gate structure that had apolysilicon layer pattern doped with P type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:3. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withP type impurities.

Comparative Example 2

A transistor of Comparative Example 2 had a gate insulation layer formedon a substrate. The transistor included a gate structure that had apolysilicon layer pattern doped with N type impurities, a tungstensilicide layer pattern, a barrier layer pattern, a metal layer patternand a hard mask pattern sequentially formed on the gate insulationlayer. Here, the tungsten silicide layer pattern included tungsten andsilicon with an atomic ratio of about 1:3. The transistor furtherincluded source/drain regions formed at portions of the substrateadjacent to the gate structure. The source/drain regions were doped withN type impurities.

Evaluation of Profiles of Transistors According to Examples 1 and 2 andComparative Example 1

FIGS. 9 and 10 are electron microscopic photographs showing gatestructures according to Examples 1 and 2. FIG. 11 is an electronmicroscopic photograph showing a gate structure according to ComparativeExample 1. In FIGS. 9 to 11, the electron microscopic photographs wereobtained using a scanning electronic microscope (SEM).

Referring to FIGS. 9 and 10 corresponding to Examples 1 and 2respectively, tungsten layer patterns remained on tungsten silicidelayer patterns 300 a and 300 b. After forming the tungsten layerpatterns, each of the tungsten silicide layers 300 a and 300 b has athickness substantially the same as an initial thickness thereof.

However, as shown in FIG. 11 corresponding to Comparative Example 1, atungsten layer pattern formed on a tungsten silicide layer pattern 300 cwas silicided. When the tungsten layer pattern was silicided, a volumeof the tungsten layer pattern was reduced so that a void 302 wasgenerated adjacent to an interface between a polysilicon layer patternand the tungsten silicide layer pattern 300 c. Further, the thickness ofthe tungsten silicide layer pattern 300 c increased substantially whenthe tungsten silicide layer pattern 300 c was silicided. The thicknessof the polysilicon layer pattern decreased by about 50 percent of aninitial thickness thereof as a result of a silicidation reaction betweenthe tungsten layer pattern and the polysilicon layer pattern.

Evaluation of Electrical Characteristics of Transistors According toExamples 1 to 6 and Comparative Examples 1 and 2

Resistances of gate structures in the transistors of Examples 1 to 6 andComparative Examples 1 and 2 were measured. The measured resistances areshown in the following Tables 1 and 2.

TABLE 1 Comparative Example 1 Example 2 Example 3 Example 1 Resistanceof Gate 1.8 × 10⁵ 6.0 × 10⁴ 1.7 × 10⁴ Impossible to Structure [Ω]measure

TABLE 2 Comparative Example 4 Example 5 Example 6 Example 2 Resistanceof Gate 2.3 × 10⁵ 6.1 × 10⁴ 3.4 × 10⁴ Impossible to Structure [Ω]measure

Additionally, resistance of the tungsten silicide layer patterns in thegate structures of Examples 1 to 6 and Comparative Examples 1 and 2 weremeasured. The measured specific resistances are shown in the followingTable 3.

TABLE 3 Specific Resistance of Tungsten Silicide Layer Pattern [μΩcm]Examples 1 and 5 About 53,000 Examples 2 and 4 About 16,000 Examples 3and 6 About 8,000 Comparative Examples 1 and 2 About 2,000

As shown in Tables 1 and 2, the resistance of the gate structures of thetransistors decreased as the content of silicon in the tungsten silicidelayer patterns was increased. Particularly, the resistance of the gatestructures according to Example 3 and 6 were relatively small becauseeach of the tungsten silicide layer patterns of Examples 3 and 6included tungsten and silicon by the atomic ratio of about 1:8.

In the Comparative Examples 1 and 2, since the tungsten layer patternsof the gate structures were partially silicided, the resistance of thegate electrodes measured at different regions was considerably differentfrom one another. Thus, the gate structures according to ComparativeExamples 1 and 2 did not show exact resistances.

As shown in Table 3, the resistances of the gate structures were reducedaccording as the specific resistances of the tungsten silicide layerpatterns were decreased.

As described above, the profile and the electrical characteristics ofthe gate structure may depend heavily on the composition of a tungstensilicide layer pattern disposed between a polysilicon layer pattern anda metal layer pattern as an ohmic layer pattern. For example, when atungsten silicide layer pattern includes tungsten and silicon by theatomic ratio in a range of about 1:5 to about 1.0:15.0, a gate structureof a transistor may have a substantially reduced resistance.

According to example embodiments of the present invention, a tungstensilicide layer and/or a tungsten silicide layer pattern may be used asan ohmic layer and/or an ohmic layer pattern in a conductive structure,for example, a gate structure of a transistor or a metal wiring in asemiconductor device. Accordingly, a gate structure or the metal wiringincluding an ohmic layer and/or ohmic layer pattern may have a greatlyreduced resistance. As a result, a transistor and/or a semiconductordevice may have improved response speeds and enhanced reliability.

The foregoing description of example embodiments is illustrative of thepresent invention and is not to be construed as limiting thereof.Although a few example embodiments of this invention have beendescribed, those skilled in the art will readily appreciate that manymodifications are possible in the example embodiments without materiallydeparting from the novel teachings and advantages of the presentinvention. Accordingly, all such modifications are intended to beincluded within the scope of the present invention as defined in theclaims. In the claims, means-plus-function clauses are intended to coverthe structures described herein as performing the recited function andnot only structural equivalents but also equivalent structures.Therefore, it is to be understood that the foregoing is illustrative ofthe present invention and is not to be construed as limited to thespecific embodiments disclosed, and that modifications to the disclosedembodiments, as well as other embodiments, are intended to be includedwithin the scope of the appended claims.

1. A semiconductor device, comprising: a first conductive layer providedon a substrate; a tungsten silicide layer including tungsten and siliconwith an atomic ratio within a range of about 1:5 to about 1:15; abarrier layer provided on the tungsten silicide layer; and a tungstenlayer provided on the barrier layer, wherein the tungsten silicide layerprevents a silicidation of the tungsten layer and reduces a contactresistance between the first conductive layer and the tungsten layer. 2.The semiconductor device of claim 1, wherein the tungsten silicide layeris obtained in a chamber using a reaction gas including a tungstensource gas and a silicon source gas by a partial pressure ratio within arange of about 1.0:25.0 to about 1.0:160.0, the reaction gas having apartial pressure within a range of about 2.05 percent to about 30.0percent of a total internal pressure of the chamber.
 3. A gate structureof a transistor, comprising: a first conductive layer pattern providedon a substrate; a tungsten silicide layer pattern on the firstconductive layer pattern, the tungsten silicide layer pattern includingtungsten and silicon with an atomic ratio within a range of about 1:5 toabout 1:15; a barrier layer pattern provided on the tungsten silicidelayer pattern; and a second conductive layer pattern provided on thetungsten silicide layer pattern, the second conductive layer patternincluding tungsten, wherein the tungsten silicide layer pattern reducesa contact resistance between the first and the second conductive layerpatterns and reduces a silicidation of the second conductive layerpattern.
 4. The gate structure of claim 3, wherein the tungsten silicidelayer pattern has a thickness within a range of about 30 Å to about 200Å.
 5. The gate structure of claim 3, wherein the tungsten silicide layerpattern is obtained in a chamber using a reaction gas including atungsten source gas and a silicon source gas by a partial pressure ratiowithin a range of about 1.0:25.0 to about 1.0:160.0, the reaction gashaving a partial pressure within a range of about 2.05 percent to about30.0 percent of a total internal pressure of the chamber.
 6. A metalwiring, comprising: an insulation layer provided on a substrate; atungsten silicide layer pattern formed on a sidewall and a bottom faceof a contact hole formed through the insulation layer; a barrier layerpattern provided on the tungsten silicide layer pattern; and aconductive layer pattern provided on the barrier layer pattern to atleast partially fill the contact hole, the conductive layer patternincluding tungsten, wherein the tungsten silicide layer pattern reducesa contact resistance between the first and the second conductive layerpatterns and reduces a silicidation of the second conductive layerpattern.